Dental Glass Ionomer Cement Permanent Adhesion For Teeth Crowns Bridge Powder And Liquid.
Luting I is a truly biocompatible, quick-set, contemporary luting glass ionomer cement that ensures reliable and long-lasting restorations;
The Luting II product has most of the functions of the Luting I and Filling I products. It can be used for the same purpose as the Luting I product, and can also be used for filling caries cavity in the non-stressed area.The physical and chemical properties of Luting II products for bonding and filling are basically the same as those of Luting I and Filling I products, and the working time and compressive strength of the products for filling are better than those of Filling I;
Glass Lonomer Cement-Filling I, filling I is a true self-adhesive, bulk glass ionomer cement that ensures reliable and long-lasting restorations.
|
Description:
- Luting I is a truly biocompatible, quick-set, contemporary luting glass ionomer cement that ensures reliable and long-lasting restorations.
Advantages:
- Sustained release of fluoride ions
- Chemically bond to tooth structure for excellent edge sealing
- Optimum thixotropy and ideal film thickness
- Simple, convenient and efficient to operate
- Easier to clean than resin-bonded materials
Indication:
- Inlay/Onlay/Crown/Bridge: Ceramic/Glass Ceramic, Oxide Ceramic, Metal/Metal-Based
- Post/Screw: Metal, Oxide Ceramic
- Orthodontic Bands
Technical Parameters:
- Powder/Liquid Ratio(g/g): 1.6-1.8/1.0
- Mixing Time: 45s
- Working Time: 2min 10s
- Setting Time: 3min 05s
- Film thickness: 12μm
- Compression Strength: >150Mpa
- Shelf Life: 2 Years
Package Included:
- 30g*1 Powder
- 25g*1 Liquid
- 1* Measuring scoop
- 1* Mixing pad(50 sheets)
- 1* Instruction Manual
|
|
Description:
- The Luting II product has most of the functions of the Luting I and Filling I products. It can be used for the same purpose as the Luting I product, and can also be used for filling caries cavity in the non-stressed area.
- The physical and chemical properties of Luting II products for bonding and filling are basically the same as those of Luting I and Filling I products, and the working time and compressive strength of the products for filling are better than those of Filling I.
Indications
- Cementation of high strength (zirconia based) all ceramic crowns and bridges
- Cementation of posts and screws made of metal or high-strength ceramic
- Cementation of orthodontic bands
- Restoration of caries in unstressed area
Advantages
- When used for luting: Ideal film thickness
- When used for filling: Good durability+Low stickiness+Time saving
- High fluoride releasing largely prevents secondary caries.
- Low solubility ensures low occurrence of microleakage.
- Brilliant biocompatibility and physical-mechanical properties.
Technical Parameters
| Luting II |
For Luting |
For Filling |
| Powder/Liquid Ratio(g/g): |
1.6-1.8/1.0 |
2.3-2.5/1.0 |
| Mixing Time: |
45s |
45s |
| Working Time: |
2min 10s |
3min |
| Setting Time: |
3min 15s |
2min45s |
| Film thickness: |
13μm |
/ |
| Compression Strength: |
>140Mpa |
>180Mpa |
| Shade: |
A1 |
A1 |
| Shelf Life: |
2 years |
2 years |
Package Included:
- 30g*1 Powder
- 25g*1 Liquid
- 1*Measuring scoop
- 1*Mixing pad(50 sheets)
- 1*Instruction Manual
|
|
Description:
- Filling I is a true self-adhesive, bulk glass ionomer cement that ensures reliable and long-lasting restorations.
Advantages:
- Sustained release of fluoride ions
- High compressive strength.
- Ideal particle size distribution.
- Easy to mix and provides good operation experience.
Indication:
- Restoration of primary teeth, Class Ⅲ, Ⅴ and limited Class Ⅰ cavities.
- Base linings under composite and amalgam.
- Core build-up.
- Atraumatic restorative treatment (ART).
Technical Parameters:
- Powder/Liquid Ratio(g/g): 2.3-2.9/1.0
- Mixing Time: 1min 00s
- Working Time: 2min 20s
- Setting Time: 2min 45s
- Compression Strength: >180Mpa
- Shade: A2
- Shelf Life: 3 Years